PPG POWERCRON® P6200HE
To contact us for more information on this product click here >>
-
Description
Cationic epoxy electrocoat
-
Chemistry
Lead-free epoxy
-
Benefits
- Excellent corrosion resistance: Including on sharp edges; On various substrates
- Environmental advantages: Formulated without lead or chrome; formulated to respond to REACH legislation; reduced biological and chemical oxygen demand (BOD and COD) in the effluents
- Performance advantages: Broad film build capability; smooth film appearance; excellent chemical resistance
- OEM Approvals
-
Suggested End Uses
- Automotive Parts & Accessories
- Truck Bodies & Truck Beds
- Construction
- Trailers
- Agriculture
- Wheels
- Material handling
- Recreational vehicles
- Transportation
- Fasteners
- Retail shelving and storage
- Buses
Performance Properties
Property | Standard | Results |
---|---|---|
Pencil Hardness | ASTM D3363 | F-H |
Flexibility | T-bend, ASTM D4145 | 2 T-bend, No pick-off |
Cross Hatch Adhesion | ASTM D3359,1/16” wet and dry | Excellent - no removal |
Direct Impact | ASTM D5420, 1/10” distortion | Excellent - no removal |
Salt Spray Resistance | ASTM B117, 1500 hrs.; 5% NaCl @ 100°F | Meets or exceeds spec of 1/16" max. undercutting |
Humidity Resistance | ASTM D714; ASTM D2247, 1500 hrs.; 100% relative humidity @ 100°F | Few #8 blisters max |
Exterior Exposure | ASTM G7/G7M 1yr. @ 45°, south Florida; No loss of adhesion; ASTM D2244 Maximum 8 E color change (fade); ASTM D4214 | Maximum 6 chalk rating |
Test Results
- | - | Delamination ISO 4628-8 |
---|---|---|
Salt Spray - 1000 Hours | ISO 9227 | 0.5 – 1 mm |
PV 1210 - VW – 60 cycles | PV1210 | 1 – 1.5 mm |
VDA – 10 cycles | ISO 11997-1 cycle B | 1 – 1.5 mm |
CCT1 Nissan – 150 cycles | NES M0007-33-CCT1 | 1.5 – 2 mm |
SCAB Ford – 50 cycles | BI 123-01 | 0.5 – 1 mm |
ECC1 – Renault – 42 Cycles | D17 2028 | 3 – 3.5 mm total creep (Delamination Renault 02-00-005) |
Product Characteristics
Color | - | Black & earthtones |
Film thickness | - | 12 - 40+ μm |
Gloss @ 60°C | ISO 2813 | 40 - 80% |