PPG Duranar® Sunstorm® Coil Coatings
To contact us for more information on this product click here >>
-
Description
The Duranar Sunstorm fluoropolymer Coatings are a two coat pearlescent mica system for aluminum and steel substrates applied with a roll coating application.
-
Chemistry
Fluoropolymer (70% PVDF + 30% Acrylic)
-
Benefits
- Wide palette of pearlescent mica flake color options in two layers, custom color matching available
- Decades of proven performance
- Outstanding gloss and color retention versus polyester technology
- Exceptional film integrity, color fade, chalk resistance
- Strong corrosion resistance
-
Suggested End Uses
- Building panels
- High-end storefronts
- Curtain walls
- Roof panels
- Aluminum composite and accent trim
Product Characteristics
Product Characteristic | Test Standard | Aluminum substrate | Coated steel substrate |
---|---|---|---|
Dry Film Thickness (Nominal) | ASTM D1400 | 0.20-0.30 mil primer; 0.70-0.80 mil color/metallic; 0.45-0.55 mil clear topcoat | 0.20-0.30 mil primer; 0.70-0.80 mil color/metallic; 0.45-0.55 mil clear topcoat |
Gloss | ASTM D523 Standard @ 60° | 25-35 | 25-35 |
Gloss | ASTM D523 Low gloss @ 85° | <10 | <10 |
Technical Properties
1 Coated Steel includes the following types of steel: G90 hot dip galvanized, Galvalume®, and Zincalume®. 2 Fracturing or rupturing of substrate will rupture coatings. Heavy gauge and clad steel substrates impose limitations on formability 3 Corrosion performance is dependent on properly cleaned and pretreated substrate These test results are based on methods believed to be correct and were performed on laboratory prepared panels. This document is not a guarantee of future.
Property | Test Standard | Aluminum substrate | Coated steel substrate |
---|---|---|---|
Pencil Hardness | ASTM D3363 | F min - 2H | F min - 2H |
Flexibility (T-Bend)2 | ASTM D4145 | 2 T-bend, no pick-off | 2 T-bend, no pick-off |
Adhesion | ASTM D3359 | No adhesion loss | No adhesion loss |
Reverse Impact | ASTM D2794: 1.5 x metal thickness (aluminum); 3.0 x metal thickness (coated steel) | No cracking or adhesion loss | No cracking or adhesion loss |
Acid Resistance | ASTM D1308: 10% muriatic acid – 24 hours; 20% sulfuric acid – 18 hours | No effect | No effect |
Acid Rain Test | Kesternich SO2, DIN 50018 | 15 cycles minimum; No objectionable changes | 15 cycles minimum; No objectionable changes |
Alkali Resistance | ASTM D1308: 10%, 20% NaOH, 1 hour | No effect | No effect |
Salt Spray Resistance | ASTM B117: 5% salt fog @ 95°F / 35°C | None or few #8 blisters; > 1/16” scribe creep average; Passes 4,000 hrs. | None or few #8 blisters; > 1/16" scribe creep average; Passes 1,000 hrs. |
Humidity Resistance | ASTM D714, ASTM D2247: 100% relative humidity @ 95°F / 35°C | Passes 4,000 hrs; None or few #8 blisters | Passes 1,500 hrs; None or few #8 blisters |
Exterior Exposure (10 Years @ 45° South Florida) | ASTM D2244, ASTM D4214 | Max. 5 fade; Max. 8 chalk | Max. 5 fade; Max. 8 chalk |